AWS BAg-7 vs. Grade 363 Molybdenum

Both AWS BAg-7 and grade 363 molybdenum are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-7 and the bottom bar is grade 363 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
310
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 31
120
Tensile Strength: Ultimate (UTS), MPa 150
580 to 720

Thermal Properties

Latent Heat of Fusion, J/g 130
370
Specific Heat Capacity, J/kg-K 290
250
Thermal Expansion, µm/m-K 20
7.0

Otherwise Unclassified Properties

Density, g/cm3 9.3
10
Embodied Carbon, kg CO2/kg material 55
28
Embodied Energy, MJ/kg 860
330

Common Calculations

Stiffness to Weight: Axial, points 4.9
17
Stiffness to Weight: Bending, points 16
22
Strength to Weight: Axial, points 4.5
16 to 20
Strength to Weight: Bending, points 6.7
15 to 17
Thermal Shock Resistance, points 6.4
19 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.010 to 0.030
Copper (Cu), % 21 to 23
0
Iron (Fe), % 0
0 to 0.010
Molybdenum (Mo), % 0
99.3 to 99.5
Nickel (Ni), % 0
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0030
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 55 to 57
0
Tin (Sn), % 4.5 to 5.5
0
Titanium (Ti), % 0
0.4 to 0.55
Zinc (Zn), % 15 to 19
0
Zirconium (Zr), % 0
0.060 to 0.12
Residuals, % 0 to 0.15
0