AWS BAg-7 vs. Grade 702C Zirconium

Both AWS BAg-7 and grade 702C zirconium are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-7 and the bottom bar is grade 702C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
97
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 31
36
Tensile Strength: Ultimate (UTS), MPa 150
430

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Specific Heat Capacity, J/kg-K 290
270
Thermal Expansion, µm/m-K 20
5.7

Otherwise Unclassified Properties

Density, g/cm3 9.3
6.7

Common Calculations

Stiffness to Weight: Axial, points 4.9
8.1
Stiffness to Weight: Bending, points 16
23
Strength to Weight: Axial, points 4.5
18
Strength to Weight: Bending, points 6.7
19
Thermal Shock Resistance, points 6.4
55

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 21 to 23
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0
0 to 0.3
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0
0 to 0.010
Silver (Ag), % 55 to 57
0
Tin (Sn), % 4.5 to 5.5
0
Zinc (Zn), % 15 to 19
0
Zirconium (Zr), % 0
94.8 to 100
Residuals, % 0 to 0.15
0