Both AWS BAg-7 and solder alloy 701 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-7 and the bottom bar is solder alloy 701.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
51
Poisson's Ratio 0.34
0.36
Shear Modulus, GPa 31
19
Tensile Strength: Ultimate (UTS), MPa 150
54

Thermal Properties

Latent Heat of Fusion, J/g 130
61
Melting Completion (Liquidus), °C 650
230
Melting Onset (Solidus), °C 620
220
Specific Heat Capacity, J/kg-K 290
220
Thermal Expansion, µm/m-K 20
22

Otherwise Unclassified Properties

Density, g/cm3 9.3
7.4
Embodied Carbon, kg CO2/kg material 55
18
Embodied Energy, MJ/kg 860
300

Common Calculations

Stiffness to Weight: Axial, points 4.9
3.8
Stiffness to Weight: Bending, points 16
17
Strength to Weight: Axial, points 4.5
2.0
Strength to Weight: Bending, points 6.7
4.3
Thermal Shock Resistance, points 6.4
3.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 21 to 23
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 55 to 57
3.5 to 3.9
Tin (Sn), % 4.5 to 5.5
95.6 to 96.5
Zinc (Zn), % 15 to 19
0 to 0.0010
Residuals, % 0 to 0.15
0