AWS BAg-7 vs. R60706 Alloy

Both AWS BAg-7 and R60706 alloy are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-7 and the bottom bar is R60706 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
98
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 31
37
Tensile Strength: Ultimate (UTS), MPa 150
580

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Specific Heat Capacity, J/kg-K 290
270
Thermal Expansion, µm/m-K 20
6.3

Otherwise Unclassified Properties

Density, g/cm3 9.3
6.7

Common Calculations

Stiffness to Weight: Axial, points 4.9
8.1
Stiffness to Weight: Bending, points 16
23
Strength to Weight: Axial, points 4.5
24
Strength to Weight: Bending, points 6.7
23
Thermal Shock Resistance, points 6.4
67

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.2
Copper (Cu), % 21 to 23
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0
0 to 0.2
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.16
Silver (Ag), % 55 to 57
0
Tin (Sn), % 4.5 to 5.5
0
Zinc (Zn), % 15 to 19
0
Zirconium (Zr), % 0
91 to 98
Residuals, % 0 to 0.15
0