AWS BAg-8 vs. Solder Alloy 114

Both AWS BAg-8 and solder alloy 114 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-8 and the bottom bar is solder alloy 114.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 84
30
Poisson's Ratio 0.36
0.41
Shear Modulus, GPa 31
11
Tensile Strength: Ultimate (UTS), MPa 150
37

Thermal Properties

Latent Heat of Fusion, J/g 140
38
Melting Completion (Liquidus), °C 780
240
Melting Onset (Solidus), °C 780
180
Specific Heat Capacity, J/kg-K 280
170
Thermal Expansion, µm/m-K 19
26

Otherwise Unclassified Properties

Density, g/cm3 10
9.7

Common Calculations

Stiffness to Weight: Axial, points 4.6
1.7
Stiffness to Weight: Bending, points 14
11
Strength to Weight: Axial, points 4.1
1.1
Strength to Weight: Bending, points 6.2
2.6
Thermal Shock Resistance, points 6.7
3.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 26.9 to 29
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
58.4 to 60.5
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 71 to 73
0 to 0.1
Tin (Sn), % 0
39.5 to 40.5
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.15
0