MakeItFrom.com
Menu (ESC)

AWS BAg-8 vs. R04295 Alloy

Both AWS BAg-8 and R04295 alloy are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-8 and the bottom bar is R04295 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 84
100
Poisson's Ratio 0.36
0.38
Shear Modulus, GPa 31
37
Tensile Strength: Ultimate (UTS), MPa 150
410

Thermal Properties

Latent Heat of Fusion, J/g 140
300
Specific Heat Capacity, J/kg-K 280
260
Thermal Expansion, µm/m-K 19
7.2

Otherwise Unclassified Properties

Density, g/cm3 10
9.0

Common Calculations

Stiffness to Weight: Axial, points 4.6
6.3
Stiffness to Weight: Bending, points 14
17
Strength to Weight: Axial, points 4.1
13
Strength to Weight: Bending, points 6.2
14
Thermal Shock Resistance, points 6.7
40

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.015
Copper (Cu), % 26.9 to 29
0
Hafnium (Hf), % 0
9.0 to 11
Hydrogen (H), % 0
0 to 0.0015
Niobium (Nb), % 0
85.9 to 90.3
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.025
Silver (Ag), % 71 to 73
0
Tantalum (Ta), % 0
0 to 0.5
Titanium (Ti), % 0
0.7 to 1.3
Tungsten (W), % 0
0 to 0.5
Zirconium (Zr), % 0
0 to 0.7
Residuals, % 0 to 0.15
0