AWS BAg-9 vs. EN 1.4335 Stainless Steel

AWS BAg-9 belongs to the otherwise unclassified metals classification, while EN 1.4335 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is EN 1.4335 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.35
0.27
Shear Modulus, GPa 31
79
Tensile Strength: Ultimate (UTS), MPa 140
570

Thermal Properties

Latent Heat of Fusion, J/g 130
300
Melting Completion (Liquidus), °C 720
1410
Melting Onset (Solidus), °C 670
1370
Specific Heat Capacity, J/kg-K 290
480
Thermal Expansion, µm/m-K 20
16

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.9
Embodied Energy, MJ/kg 980
62

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.1
20
Strength to Weight: Bending, points 6.3
19
Thermal Shock Resistance, points 6.0
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
49.4 to 56
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0
20 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.25
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0