AWS BAg-9 vs. EN 1.4848 Stainless Steel

AWS BAg-9 belongs to the otherwise unclassified metals classification, while EN 1.4848 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is EN 1.4848 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 31
78
Tensile Strength: Ultimate (UTS), MPa 140
510

Thermal Properties

Latent Heat of Fusion, J/g 130
320
Melting Completion (Liquidus), °C 720
1390
Melting Onset (Solidus), °C 670
1340
Specific Heat Capacity, J/kg-K 290
490
Thermal Expansion, µm/m-K 20
16

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.8
Embodied Energy, MJ/kg 980
63

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.1
18
Strength to Weight: Bending, points 6.3
18
Thermal Shock Resistance, points 6.0
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.3 to 0.5
Chromium (Cr), % 0
24 to 27
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
45.4 to 55.7
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
19 to 22
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
1.0 to 2.5
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0