AWS BAg-9 belongs to the otherwise unclassified metals classification, while EN 1.7239 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is EN 1.7239 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
190
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 31
73
Tensile Strength: Ultimate (UTS), MPa 140
660 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Melting Completion (Liquidus), °C 720
1460
Melting Onset (Solidus), °C 670
1410
Specific Heat Capacity, J/kg-K 290
470
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.8
Embodied Energy, MJ/kg 980
20

Common Calculations

Stiffness to Weight: Axial, points 4.8
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.1
23 to 71
Strength to Weight: Bending, points 6.3
21 to 45
Thermal Shock Resistance, points 6.0
19 to 59

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.56 to 0.64
Chromium (Cr), % 0
0.7 to 1.0
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
96.8 to 98
Manganese (Mn), % 0
0.7 to 1.0
Molybdenum (Mo), % 0
0.060 to 0.15
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0