AWS BAg-9 vs. SAE-AISI 1086 Steel

AWS BAg-9 belongs to the otherwise unclassified metals classification, while SAE-AISI 1086 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is SAE-AISI 1086 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
190
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 31
72
Tensile Strength: Ultimate (UTS), MPa 140
760 to 870

Thermal Properties

Latent Heat of Fusion, J/g 130
240
Melting Completion (Liquidus), °C 720
1460
Melting Onset (Solidus), °C 670
1410
Specific Heat Capacity, J/kg-K 290
470
Thermal Expansion, µm/m-K 20
11

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.8
Embodied Energy, MJ/kg 980
19

Common Calculations

Stiffness to Weight: Axial, points 4.8
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.1
27 to 31
Strength to Weight: Bending, points 6.3
24 to 26
Thermal Shock Resistance, points 6.0
26 to 30

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.8 to 0.93
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
98.5 to 98.9
Manganese (Mn), % 0
0.3 to 0.5
Phosphorus (P), % 0
0 to 0.040
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.050
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0