AWS BAg-9 vs. SAE-AISI D7 Steel

AWS BAg-9 belongs to the otherwise unclassified metals classification, while SAE-AISI D7 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is SAE-AISI D7 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
190
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 31
73
Tensile Strength: Ultimate (UTS), MPa 140
800 to 2120

Thermal Properties

Latent Heat of Fusion, J/g 130
270
Melting Completion (Liquidus), °C 720
1440
Melting Onset (Solidus), °C 670
1400
Specific Heat Capacity, J/kg-K 290
480
Thermal Expansion, µm/m-K 20
11

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.6
Embodied Energy, MJ/kg 980
180

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.1
29 to 78
Strength to Weight: Bending, points 6.3
25 to 48
Thermal Shock Resistance, points 6.0
27 to 72

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
2.2 to 2.5
Chromium (Cr), % 0
11.5 to 13.5
Copper (Cu), % 19 to 21
0 to 0.25
Iron (Fe), % 0
76.6 to 81.9
Manganese (Mn), % 0
0 to 0.6
Molybdenum (Mo), % 0
0.7 to 1.2
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.6
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
3.8 to 4.4
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0