AWS BAg-9 vs. SAE-AISI F2 Steel

AWS BAg-9 belongs to the otherwise unclassified metals classification, while SAE-AISI F2 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is SAE-AISI F2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
190
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 31
73
Tensile Strength: Ultimate (UTS), MPa 140
710 to 2360

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Melting Completion (Liquidus), °C 720
1520
Melting Onset (Solidus), °C 670
1470
Specific Heat Capacity, J/kg-K 290
460
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Density, g/cm3 9.6
8.1
Embodied Energy, MJ/kg 980
32

Common Calculations

Stiffness to Weight: Axial, points 4.8
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.1
24 to 81
Strength to Weight: Bending, points 6.3
22 to 49
Thermal Shock Resistance, points 6.0
21 to 71

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
1.2 to 1.4
Chromium (Cr), % 0
0.2 to 0.4
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
92.6 to 95.4
Manganese (Mn), % 0
0.1 to 0.5
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.1 to 0.5
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
3.0 to 4.5
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0