AWS BAg-9 vs. C19010 Copper

AWS BAg-9 belongs to the otherwise unclassified metals classification, while C19010 copper belongs to the copper alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is C19010 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
120
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 31
43
Tensile Strength: Ultimate (UTS), MPa 140
330 to 640

Thermal Properties

Latent Heat of Fusion, J/g 130
210
Melting Completion (Liquidus), °C 720
1060
Melting Onset (Solidus), °C 670
1010
Specific Heat Capacity, J/kg-K 290
390
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 9.6
8.9
Embodied Energy, MJ/kg 980
42

Common Calculations

Stiffness to Weight: Axial, points 4.8
7.3
Stiffness to Weight: Bending, points 15
18
Strength to Weight: Axial, points 4.1
10 to 20
Strength to Weight: Bending, points 6.3
12 to 18
Thermal Shock Resistance, points 6.0
12 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 19 to 21
97.3 to 99.04
Nickel (Ni), % 0
0.8 to 1.8
Phosphorus (P), % 0
0.010 to 0.050
Silicon (Si), % 0
0.15 to 0.35
Silver (Ag), % 64 to 66
0
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0 to 0.5