AWS BAg-9 vs. C74000 Nickel Silver

AWS BAg-9 belongs to the otherwise unclassified metals classification, while C74000 nickel silver belongs to the copper alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is C74000 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
120
Poisson's Ratio 0.35
0.32
Shear Modulus, GPa 31
44
Tensile Strength: Ultimate (UTS), MPa 140
380 to 590

Thermal Properties

Latent Heat of Fusion, J/g 130
200
Melting Completion (Liquidus), °C 720
990
Melting Onset (Solidus), °C 670
950
Specific Heat Capacity, J/kg-K 290
390
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 9.6
8.5
Embodied Energy, MJ/kg 980
54

Common Calculations

Stiffness to Weight: Axial, points 4.8
7.7
Stiffness to Weight: Bending, points 15
19
Strength to Weight: Axial, points 4.1
13 to 19
Strength to Weight: Bending, points 6.3
14 to 18
Thermal Shock Resistance, points 6.0
13 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 19 to 21
69 to 73.5
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0
9.0 to 11
Silver (Ag), % 64 to 66
0
Zinc (Zn), % 13 to 17
14.2 to 22
Residuals, % 0 to 0.15
0 to 0.5