AWS BAg-9 vs. R05200 Tantalum
Both AWS BAg-9 and R05200 tantalum are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-9 and the bottom bar is R05200 tantalum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 190 |
| Poisson's Ratio | 0.35 | |
| 0.34 |
| Shear Modulus, GPa | 31 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 210 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 140 |
| Thermal Expansion, µm/m-K | 20 | |
| 6.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.6 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 6.2 |
| Stiffness to Weight: Bending, points | 15 | |
| 11 |
| Strength to Weight: Axial, points | 4.1 | |
| 3.6 to 9.0 |
| Strength to Weight: Bending, points | 6.3 | |
| 4.8 to 8.8 |
| Thermal Shock Resistance, points | 6.0 | |
| 13 to 32 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 19 to 21 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 0 | |
| 0 to 0.010 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Silver (Ag), % | 64 to 66 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 99.8 to 100 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 13 to 17 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |