AWS BAg-9 vs. S30615 Stainless Steel

AWS BAg-9 belongs to the otherwise unclassified metals classification, while S30615 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-9 and the bottom bar is S30615 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
190
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 31
75
Tensile Strength: Ultimate (UTS), MPa 140
690

Thermal Properties

Latent Heat of Fusion, J/g 130
340
Melting Completion (Liquidus), °C 720
1370
Melting Onset (Solidus), °C 670
1320
Specific Heat Capacity, J/kg-K 290
500
Thermal Expansion, µm/m-K 20
16

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.6
Embodied Energy, MJ/kg 980
53

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.1
25
Strength to Weight: Bending, points 6.3
23
Thermal Shock Resistance, points 6.0
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.8 to 1.5
Carbon (C), % 0
0.16 to 0.24
Chromium (Cr), % 0
17 to 19.5
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
56.7 to 65.3
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
13.5 to 16
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
3.2 to 4.0
Silver (Ag), % 64 to 66
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 13 to 17
0
Residuals, % 0 to 0.15
0