AWS BAu-1 vs. AWS BAu-3
Both AWS BAu-1 and AWS BAu-3 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAu-1 and the bottom bar is AWS BAu-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.37 | |
| 0.37 |
| Shear Modulus, GPa | 40 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 220 |
Thermal Properties
| Brazing Temperature, °C | 1020 to 1090 | |
| 1030 to 1090 |
| Latent Heat of Fusion, J/g | 150 | |
| 160 |
| Melting Completion (Liquidus), °C | 1020 | |
| 1030 |
| Melting Onset (Solidus), °C | 990 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 300 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 13 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.7 | |
| 5.0 |
| Stiffness to Weight: Bending, points | 12 | |
| 13 |
| Strength to Weight: Axial, points | 4.5 | |
| 4.9 |
| Strength to Weight: Bending, points | 6.1 | |
| 6.4 |
| Thermal Shock Resistance, points | 8.5 | |
| 8.7 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 61.9 to 63 | |
| 60.9 to 63 |
| Gold (Au), % | 37 to 38 | |
| 34.5 to 35.5 |
| Nickel (Ni), % | 0 | |
| 2.5 to 3.5 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |