AWS BAu-1 vs. Grade 702C Zirconium

Both AWS BAu-1 and grade 702C zirconium are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAu-1 and the bottom bar is grade 702C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
97
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 40
36
Tensile Strength: Ultimate (UTS), MPa 210
430

Thermal Properties

Latent Heat of Fusion, J/g 150
250
Specific Heat Capacity, J/kg-K 290
270
Thermal Expansion, µm/m-K 16
5.7

Otherwise Unclassified Properties

Density, g/cm3 13
6.7

Common Calculations

Stiffness to Weight: Axial, points 4.7
8.1
Stiffness to Weight: Bending, points 12
23
Strength to Weight: Axial, points 4.5
18
Strength to Weight: Bending, points 6.1
19
Thermal Shock Resistance, points 8.5
55

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 61.9 to 63
0
Gold (Au), % 37 to 38
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0
0 to 0.3
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0
0 to 0.010
Zirconium (Zr), % 0
94.8 to 100
Residuals, % 0 to 0.15
0