AWS BAu-3 vs. Solder Alloy 122

Both AWS BAu-3 and solder alloy 122 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS BAu-3 and the bottom bar is solder alloy 122.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
20
Poisson's Ratio 0.37
0.43
Shear Modulus, GPa 41
6.9
Tensile Strength: Ultimate (UTS), MPa 220
30

Thermal Properties

Latent Heat of Fusion, J/g 160
27
Melting Completion (Liquidus), °C 1030
300
Melting Onset (Solidus), °C 970
270
Specific Heat Capacity, J/kg-K 300
140
Thermal Expansion, µm/m-K 16
28

Otherwise Unclassified Properties

Density, g/cm3 13
11

Common Calculations

Stiffness to Weight: Axial, points 5.0
1.0
Stiffness to Weight: Bending, points 13
8.2
Strength to Weight: Axial, points 4.9
0.77
Strength to Weight: Bending, points 6.4
2.0
Thermal Shock Resistance, points 8.7
3.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 60.9 to 63
0 to 0.080
Gold (Au), % 34.5 to 35.5
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
88.4 to 90.5
Nickel (Ni), % 2.5 to 3.5
0 to 0.010
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
9.5 to 10.5
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.15
0