AWS BAu-6 vs. AWS BVPd-1
Both AWS BAu-6 and AWS BVPd-1 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition.
For each property being compared, the top bar is AWS BAu-6 and the bottom bar is AWS BVPd-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 150 |
| Poisson's Ratio | 0.39 | |
| 0.37 |
| Shear Modulus, GPa | 43 | |
| 56 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 240 |
Thermal Properties
| Brazing Temperature, °C | 1050 to 1120 | |
| 1240 to 1250 |
| Latent Heat of Fusion, J/g | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1240 |
| Melting Onset (Solidus), °C | 1010 | |
| 1230 |
| Specific Heat Capacity, J/kg-K | 210 | |
| 310 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 16 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.0 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 10 | |
| 16 |
| Strength to Weight: Axial, points | 3.2 | |
| 6.1 |
| Strength to Weight: Bending, points | 4.5 | |
| 7.9 |
| Thermal Shock Resistance, points | 8.5 | |
| 9.8 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Cadmium (Cd), % | 0 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 | |
| 0 to 0.0050 |
| Cobalt (Co), % | 0 | |
| 33.9 to 36 |
| Gold (Au), % | 69.5 to 70.5 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.0020 |
| Nickel (Ni), % | 21.5 to 22.5 | |
| 0 to 0.060 |
| Palladium (Pd), % | 7.5 to 8.5 | |
| 64 to 66 |
| Phosphorus (P), % | 0 | |
| 0 to 0.0020 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.15 | |
| 0 |