AWS BCo-1 vs. Nickel 689
AWS BCo-1 belongs to the cobalt alloys classification, while nickel 689 belongs to the nickel alloys. They have 47% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS BCo-1 and the bottom bar is nickel 689.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 700 | |
| 1250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 330 |
| Melting Completion (Liquidus), °C | 1150 | |
| 1440 |
| Melting Onset (Solidus), °C | 1120 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 11 |
| Embodied Energy, MJ/kg | 110 | |
| 150 |
| Embodied Water, L/kg | 430 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 | |
| 41 |
| Strength to Weight: Bending, points | 22 | |
| 30 |
| Thermal Shock Resistance, points | 21 | |
| 35 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.050 | |
| 0.75 to 1.3 |
| Boron (B), % | 0.7 to 0.9 | |
| 0.0030 to 0.010 |
| Carbon (C), % | 0.35 to 0.45 | |
| 0.1 to 0.2 |
| Chromium (Cr), % | 18 to 20 | |
| 18 to 20 |
| Cobalt (Co), % | 46 to 54 | |
| 9.0 to 11 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 10.5 |
| Nickel (Ni), % | 16 to 18 | |
| 48.3 to 60.9 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.015 |
| Selenium (Se), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 7.5 to 8.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 to 0.050 | |
| 2.3 to 2.8 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |