AWS BMg-1 vs. AWS BAg-7

AWS BMg-1 belongs to the magnesium alloys classification, while AWS BAg-7 belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BMg-1 and the bottom bar is AWS BAg-7.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 47
83
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 18
31
Tensile Strength: Ultimate (UTS), MPa 180
150

Thermal Properties

Brazing Temperature, °C 600 to 630
650 to 900
Latent Heat of Fusion, J/g 350
130
Melting Completion (Liquidus), °C 600
650
Melting Onset (Solidus), °C 440
620
Specific Heat Capacity, J/kg-K 980
290
Thermal Expansion, µm/m-K 26
20

Otherwise Unclassified Properties

Density, g/cm3 1.8
9.3
Embodied Carbon, kg CO2/kg material 22
55
Embodied Energy, MJ/kg 160
860

Common Calculations

Stiffness to Weight: Axial, points 14
4.9
Stiffness to Weight: Bending, points 66
16
Strength to Weight: Axial, points 27
4.5
Strength to Weight: Bending, points 39
6.7
Thermal Shock Resistance, points 10
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
0
Beryllium (Be), % 0.00020 to 0.00080
0
Copper (Cu), % 0 to 0.050
21 to 23
Iron (Fe), % 0 to 0.0050
0
Magnesium (Mg), % 86.1 to 89.8
0
Manganese (Mn), % 0.15 to 1.5
0
Nickel (Ni), % 0 to 0.0050
0
Silicon (Si), % 0 to 0.050
0
Silver (Ag), % 0
55 to 57
Tin (Sn), % 0
4.5 to 5.5
Zinc (Zn), % 1.7 to 2.3
15 to 19
Residuals, % 0 to 0.3
0 to 0.15