AWS BMg-1 vs. EN 1.3505 Steel

AWS BMg-1 belongs to the magnesium alloys classification, while EN 1.3505 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BMg-1 and the bottom bar is EN 1.3505 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 47
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
72
Tensile Strength: Ultimate (UTS), MPa 180
600 to 690

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 130
430
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 440
1410
Specific Heat Capacity, J/kg-K 980
470
Thermal Conductivity, W/m-K 76
45
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 55
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.4
Density, g/cm3 1.8
7.8
Embodied Carbon, kg CO2/kg material 22
1.5
Embodied Energy, MJ/kg 160
20
Embodied Water, L/kg 980
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 66
24
Strength to Weight: Axial, points 27
22 to 25
Strength to Weight: Bending, points 39
20 to 22
Thermal Diffusivity, mm2/s 43
12
Thermal Shock Resistance, points 10
18 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
0 to 0.050
Beryllium (Be), % 0.00020 to 0.00080
0
Carbon (C), % 0
0.93 to 1.1
Chromium (Cr), % 0
1.4 to 1.6
Copper (Cu), % 0 to 0.050
0 to 0.3
Iron (Fe), % 0 to 0.0050
97.1 to 98.3
Magnesium (Mg), % 86.1 to 89.8
0
Manganese (Mn), % 0.15 to 1.5
0.25 to 0.45
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0 to 0.0050
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.050
0.15 to 0.35
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 1.7 to 2.3
0
Residuals, % 0 to 0.3
0