AWS BMg-1 vs. SAE-AISI S1 Steel

AWS BMg-1 belongs to the magnesium alloys classification, while SAE-AISI S1 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BMg-1 and the bottom bar is SAE-AISI S1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 47
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
73
Tensile Strength: Ultimate (UTS), MPa 180
690 to 1840

Thermal Properties

Latent Heat of Fusion, J/g 350
260
Melting Completion (Liquidus), °C 600
1500
Melting Onset (Solidus), °C 440
1450
Specific Heat Capacity, J/kg-K 980
470
Thermal Conductivity, W/m-K 76
41
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 55
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
8.0
Density, g/cm3 1.8
8.0
Embodied Carbon, kg CO2/kg material 22
2.6
Embodied Energy, MJ/kg 160
37
Embodied Water, L/kg 980
56

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 66
24
Strength to Weight: Axial, points 27
24 to 64
Strength to Weight: Bending, points 39
22 to 42
Thermal Diffusivity, mm2/s 43
11
Thermal Shock Resistance, points 10
21 to 56

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
0
Beryllium (Be), % 0.00020 to 0.00080
0
Carbon (C), % 0
0.4 to 0.55
Chromium (Cr), % 0
1.0 to 1.8
Copper (Cu), % 0 to 0.050
0 to 0.25
Iron (Fe), % 0 to 0.0050
91.6 to 96.7
Magnesium (Mg), % 86.1 to 89.8
0
Manganese (Mn), % 0.15 to 1.5
0.1 to 0.4
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.0050
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.050
0.15 to 1.2
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
1.5 to 3.0
Vanadium (V), % 0
0.15 to 0.3
Zinc (Zn), % 1.7 to 2.3
0
Residuals, % 0 to 0.3
0