AWS BMg-1 vs. C48200 Brass

AWS BMg-1 belongs to the magnesium alloys classification, while C48200 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BMg-1 and the bottom bar is C48200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 47
100
Elongation at Break, % 3.8
15 to 40
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 18
40
Shear Strength, MPa 100
260 to 300
Tensile Strength: Ultimate (UTS), MPa 180
400 to 500
Tensile Strength: Yield (Proof), MPa 110
160 to 320

Thermal Properties

Latent Heat of Fusion, J/g 350
170
Maximum Temperature: Mechanical, °C 130
120
Melting Completion (Liquidus), °C 600
900
Melting Onset (Solidus), °C 440
890
Specific Heat Capacity, J/kg-K 980
380
Thermal Conductivity, W/m-K 76
120
Thermal Expansion, µm/m-K 26
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
26
Electrical Conductivity: Equal Weight (Specific), % IACS 55
29

Otherwise Unclassified Properties

Base Metal Price, % relative 12
23
Density, g/cm3 1.8
8.0
Embodied Carbon, kg CO2/kg material 22
2.7
Embodied Energy, MJ/kg 160
47
Embodied Water, L/kg 980
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.9
61 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 120
120 to 500
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 66
19
Strength to Weight: Axial, points 27
14 to 17
Strength to Weight: Bending, points 39
15 to 17
Thermal Diffusivity, mm2/s 43
38
Thermal Shock Resistance, points 10
13 to 16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
0
Beryllium (Be), % 0.00020 to 0.00080
0
Copper (Cu), % 0 to 0.050
59 to 62
Iron (Fe), % 0 to 0.0050
0 to 0.1
Lead (Pb), % 0
0.4 to 1.0
Magnesium (Mg), % 86.1 to 89.8
0
Manganese (Mn), % 0.15 to 1.5
0
Nickel (Ni), % 0 to 0.0050
0
Silicon (Si), % 0 to 0.050
0
Tin (Sn), % 0
0.5 to 1.0
Zinc (Zn), % 1.7 to 2.3
35.5 to 40.1
Residuals, % 0 to 0.3
0 to 0.4