AWS BMg-1 vs. C61500 Bronze

AWS BMg-1 belongs to the magnesium alloys classification, while C61500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BMg-1 and the bottom bar is C61500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 47
110
Elongation at Break, % 3.8
3.0 to 55
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 18
42
Shear Strength, MPa 100
350 to 550
Tensile Strength: Ultimate (UTS), MPa 180
480 to 970
Tensile Strength: Yield (Proof), MPa 110
150 to 720

Thermal Properties

Latent Heat of Fusion, J/g 350
220
Maximum Temperature: Mechanical, °C 130
220
Melting Completion (Liquidus), °C 600
1040
Melting Onset (Solidus), °C 440
1030
Specific Heat Capacity, J/kg-K 980
430
Thermal Conductivity, W/m-K 76
58
Thermal Expansion, µm/m-K 26
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
13
Electrical Conductivity: Equal Weight (Specific), % IACS 55
13

Otherwise Unclassified Properties

Base Metal Price, % relative 12
29
Density, g/cm3 1.8
8.4
Embodied Carbon, kg CO2/kg material 22
3.2
Embodied Energy, MJ/kg 160
52
Embodied Water, L/kg 980
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.9
27 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 120
100 to 2310
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 66
19
Strength to Weight: Axial, points 27
16 to 32
Strength to Weight: Bending, points 39
16 to 26
Thermal Diffusivity, mm2/s 43
16
Thermal Shock Resistance, points 10
17 to 34

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
7.7 to 8.3
Beryllium (Be), % 0.00020 to 0.00080
0
Copper (Cu), % 0 to 0.050
89 to 90.5
Iron (Fe), % 0 to 0.0050
0
Lead (Pb), % 0
0 to 0.015
Magnesium (Mg), % 86.1 to 89.8
0
Manganese (Mn), % 0.15 to 1.5
0
Nickel (Ni), % 0 to 0.0050
1.8 to 2.2
Silicon (Si), % 0 to 0.050
0
Zinc (Zn), % 1.7 to 2.3
0
Residuals, % 0 to 0.3
0 to 0.5