AWS BMg-1 vs. R58150 Titanium
AWS BMg-1 belongs to the magnesium alloys classification, while R58150 titanium belongs to the titanium alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AWS BMg-1 and the bottom bar is R58150 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 47 | |
| 140 |
| Elongation at Break, % | 3.8 | |
| 13 |
| Fatigue Strength, MPa | 72 | |
| 330 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 18 | |
| 52 |
| Shear Strength, MPa | 100 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 320 |
| Melting Completion (Liquidus), °C | 600 | |
| 1760 |
| Melting Onset (Solidus), °C | 440 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 980 | |
| 500 |
| Thermal Expansion, µm/m-K | 26 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 48 |
| Density, g/cm3 | 1.8 | |
| 5.4 |
| Embodied Carbon, kg CO2/kg material | 22 | |
| 31 |
| Embodied Energy, MJ/kg | 160 | |
| 480 |
| Embodied Water, L/kg | 980 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.9 | |
| 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 1110 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 66 | |
| 32 |
| Strength to Weight: Axial, points | 27 | |
| 40 |
| Strength to Weight: Bending, points | 39 | |
| 35 |
| Thermal Shock Resistance, points | 10 | |
| 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 8.3 to 9.7 | |
| 0 |
| Beryllium (Be), % | 0.00020 to 0.00080 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 86.1 to 89.8 | |
| 0 |
| Manganese (Mn), % | 0.15 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 14 to 16 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 83.5 to 86 |
| Zinc (Zn), % | 1.7 to 2.3 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |