AWS BNi-5a vs. R30605 Cobalt
AWS BNi-5a belongs to the nickel alloys classification, while R30605 cobalt belongs to the cobalt alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 18 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS BNi-5a and the bottom bar is R30605 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 1130 to 1900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 290 |
| Melting Completion (Liquidus), °C | 1150 | |
| 1410 |
| Melting Onset (Solidus), °C | 1070 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 410 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 9.6 |
| Embodied Carbon, kg CO2/kg material | 9.0 | |
| 9.8 |
| Embodied Energy, MJ/kg | 130 | |
| 140 |
| Embodied Water, L/kg | 260 | |
| 450 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 17 | |
| 33 to 55 |
| Strength to Weight: Bending, points | 17 | |
| 25 to 36 |
| Thermal Shock Resistance, points | 15 | |
| 31 to 52 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Boron (B), % | 1.0 to 1.5 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 18.5 to 19.5 | |
| 19 to 21 |
| Cobalt (Co), % | 0 to 0.1 | |
| 46.4 to 57 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 70.1 to 73.5 | |
| 9.0 to 11 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Selenium (Se), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 7.0 to 7.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 |
| Tungsten (W), % | 0 | |
| 14 to 16 |
| Zirconium (Zr), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |