AWS BVAg-0 vs. 70Ag-30Ni Alloy

Both AWS BVAg-0 and 70Ag-30Ni alloy are otherwise unclassified metals. They have 70% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is 70Ag-30Ni alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
100
Poisson's Ratio 0.37
0.35
Shear Modulus, GPa 26
39
Tensile Strength: Ultimate (UTS), MPa 130
320 to 530

Thermal Properties

Latent Heat of Fusion, J/g 110
170
Melting Completion (Liquidus), °C 960
960
Melting Onset (Solidus), °C 960
960
Specific Heat Capacity, J/kg-K 240
300
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 10
10

Common Calculations

Stiffness to Weight: Axial, points 3.8
5.8
Stiffness to Weight: Bending, points 13
16
Strength to Weight: Axial, points 3.4
8.8 to 15
Strength to Weight: Bending, points 5.4
10 to 15
Thermal Shock Resistance, points 6.6
13 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
0
Lead (Pb), % 0 to 0.0020
0
Nickel (Ni), % 0
28.8 to 31
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 99.95 to 100
69 to 71
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.2