AWS BVAg-0 vs. AWS BAg-13
Both AWS BVAg-0 and AWS BAg-13 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 54% of their average alloy composition in common. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is AWS BAg-13.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 91 |
| Poisson's Ratio | 0.37 | |
| 0.35 |
| Shear Modulus, GPa | 26 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 130 | |
| 180 |
Thermal Properties
| Brazing Temperature, °C | 960 to 1040 | |
| 860 to 980 |
| Latent Heat of Fusion, J/g | 110 | |
| 150 |
| Melting Completion (Liquidus), °C | 960 | |
| 860 |
| Melting Onset (Solidus), °C | 960 | |
| 720 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 310 |
| Thermal Expansion, µm/m-K | 20 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 9.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 13 | |
| 16 |
| Strength to Weight: Axial, points | 3.4 | |
| 5.2 |
| Strength to Weight: Bending, points | 5.4 | |
| 7.3 |
| Thermal Shock Resistance, points | 6.6 | |
| 7.5 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 37.4 to 42.5 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.5 to 1.5 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silver (Ag), % | 99.95 to 100 | |
| 53 to 55 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 4.0 to 6.0 |
| Residuals, % | 0 | |
| 0 to 0.15 |