AWS BVAg-0 vs. AWS BAu-6
Both AWS BVAg-0 and AWS BAu-6 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition.
For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is AWS BAu-6.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 120 |
| Poisson's Ratio | 0.37 | |
| 0.39 |
| Shear Modulus, GPa | 26 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 130 | |
| 190 |
Thermal Properties
| Brazing Temperature, °C | 960 to 1040 | |
| 1050 to 1120 |
| Latent Heat of Fusion, J/g | 110 | |
| 120 |
| Melting Completion (Liquidus), °C | 960 | |
| 1050 |
| Melting Onset (Solidus), °C | 960 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 210 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 16 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 13 | |
| 10 |
| Strength to Weight: Axial, points | 3.4 | |
| 3.2 |
| Strength to Weight: Bending, points | 5.4 | |
| 4.5 |
| Thermal Shock Resistance, points | 6.6 | |
| 8.5 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Gold (Au), % | 0 | |
| 69.5 to 70.5 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 21.5 to 22.5 |
| Palladium (Pd), % | 0 | |
| 7.5 to 8.5 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silver (Ag), % | 99.95 to 100 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |