AWS BVAg-0 vs. CC764S Brass

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while CC764S brass belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is CC764S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.31
Shear Modulus, GPa 26
41
Tensile Strength: Ultimate (UTS), MPa 130
680

Thermal Properties

Latent Heat of Fusion, J/g 110
180
Melting Completion (Liquidus), °C 960
850
Melting Onset (Solidus), °C 960
810
Specific Heat Capacity, J/kg-K 240
400
Thermal Expansion, µm/m-K 20
20

Otherwise Unclassified Properties

Density, g/cm3 10
7.9

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.6
Stiffness to Weight: Bending, points 13
20
Strength to Weight: Axial, points 3.4
24
Strength to Weight: Bending, points 5.4
22
Thermal Shock Resistance, points 6.6
22

Alloy Composition

Aluminum (Al), % 0
1.0 to 3.0
Antimony (Sb), % 0
0 to 0.050
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
52 to 66
Iron (Fe), % 0
0.5 to 2.5
Lead (Pb), % 0 to 0.0020
0 to 0.3
Manganese (Mn), % 0
0.3 to 4.0
Nickel (Ni), % 0
0 to 3.0
Phosphorus (P), % 0 to 0.0020
0 to 0.030
Silicon (Si), % 0
0 to 0.1
Silver (Ag), % 99.95 to 100
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0 to 0.0010
20.7 to 50.2