AWS BVAg-0 vs. C18100 Copper

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C18100 copper belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C18100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
120
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 26
47
Tensile Strength: Ultimate (UTS), MPa 130
510

Thermal Properties

Latent Heat of Fusion, J/g 110
210
Melting Completion (Liquidus), °C 960
1080
Melting Onset (Solidus), °C 960
1020
Specific Heat Capacity, J/kg-K 240
390
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 10
8.9

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.3
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 3.4
16
Strength to Weight: Bending, points 5.4
16
Thermal Shock Resistance, points 6.6
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Chromium (Cr), % 0
0.4 to 1.2
Copper (Cu), % 0 to 0.050
98.7 to 99.49
Lead (Pb), % 0 to 0.0020
0
Magnesium (Mg), % 0
0.030 to 0.060
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 99.95 to 100
0
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
0.080 to 0.2
Residuals, % 0
0 to 0.5