AWS BVAg-0 vs. C26200 Brass

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C26200 brass belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C26200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.31
Shear Modulus, GPa 26
41
Tensile Strength: Ultimate (UTS), MPa 130
330 to 770

Thermal Properties

Latent Heat of Fusion, J/g 110
180
Melting Completion (Liquidus), °C 960
950
Melting Onset (Solidus), °C 960
920
Specific Heat Capacity, J/kg-K 240
390
Thermal Expansion, µm/m-K 20
20

Otherwise Unclassified Properties

Density, g/cm3 10
8.2

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.2
Stiffness to Weight: Bending, points 13
19
Strength to Weight: Axial, points 3.4
11 to 26
Strength to Weight: Bending, points 5.4
13 to 23
Thermal Shock Resistance, points 6.6
11 to 26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
67 to 70
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0 to 0.0020
0 to 0.070
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 99.95 to 100
0
Zinc (Zn), % 0 to 0.0010
29.6 to 33
Residuals, % 0
0 to 0.3