AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C31400 bronze belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C31400 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.33
Shear Modulus, GPa 26
42
Tensile Strength: Ultimate (UTS), MPa 130
270 to 420

Thermal Properties

Latent Heat of Fusion, J/g 110
200
Melting Completion (Liquidus), °C 960
1040
Melting Onset (Solidus), °C 960
1010
Specific Heat Capacity, J/kg-K 240
380
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 10
8.8

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.1
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 3.4
8.7 to 13
Strength to Weight: Bending, points 5.4
11 to 14
Thermal Shock Resistance, points 6.6
9.6 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
87.5 to 90.5
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0 to 0.0020
1.3 to 2.5
Nickel (Ni), % 0
0 to 0.7
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 99.95 to 100
0
Zinc (Zn), % 0 to 0.0010
5.8 to 11.2
Residuals, % 0
0 to 0.4