AWS BVAg-0 vs. C64800 Bronze

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C64800 bronze belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C64800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
120
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 26
44
Tensile Strength: Ultimate (UTS), MPa 130
640

Thermal Properties

Latent Heat of Fusion, J/g 110
220
Melting Completion (Liquidus), °C 960
1090
Melting Onset (Solidus), °C 960
1030
Specific Heat Capacity, J/kg-K 240
390
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 10
8.9

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.4
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 3.4
20
Strength to Weight: Bending, points 5.4
19
Thermal Shock Resistance, points 6.6
23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Chromium (Cr), % 0
0 to 0.090
Cobalt (Co), % 0
1.0 to 3.0
Copper (Cu), % 0 to 0.050
92.4 to 98.8
Iron (Fe), % 0
0 to 1.0
Lead (Pb), % 0 to 0.0020
0 to 0.050
Nickel (Ni), % 0
0 to 0.5
Phosphorus (P), % 0 to 0.0020
0 to 0.5
Silicon (Si), % 0
0.2 to 1.0
Silver (Ag), % 99.95 to 100
0
Tin (Sn), % 0
0 to 0.5
Zinc (Zn), % 0 to 0.0010
0 to 0.5
Residuals, % 0
0 to 0.5