AWS BVAg-0 vs. C82000 Copper

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C82000 copper belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C82000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
120
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 26
45
Tensile Strength: Ultimate (UTS), MPa 130
350 to 690

Thermal Properties

Latent Heat of Fusion, J/g 110
220
Melting Completion (Liquidus), °C 960
1090
Melting Onset (Solidus), °C 960
970
Specific Heat Capacity, J/kg-K 240
390
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 10
8.9

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.5
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 3.4
11 to 22
Strength to Weight: Bending, points 5.4
12 to 20
Thermal Shock Resistance, points 6.6
12 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.1
Beryllium (Be), % 0
0.45 to 0.8
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Chromium (Cr), % 0
0 to 0.1
Cobalt (Co), % 0
2.2 to 2.7
Copper (Cu), % 0 to 0.050
95.2 to 97.4
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0 to 0.0020
0 to 0.020
Nickel (Ni), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.0020
0
Silicon (Si), % 0
0 to 0.15
Silver (Ag), % 99.95 to 100
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0 to 0.0010
0 to 0.1
Residuals, % 0
0 to 0.5