AWS BVAg-0 vs. C84100 Brass

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C84100 brass belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C84100 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.33
Shear Modulus, GPa 26
39
Tensile Strength: Ultimate (UTS), MPa 130
230

Thermal Properties

Latent Heat of Fusion, J/g 110
190
Melting Completion (Liquidus), °C 960
1000
Melting Onset (Solidus), °C 960
810
Specific Heat Capacity, J/kg-K 240
380
Thermal Expansion, µm/m-K 20
19

Otherwise Unclassified Properties

Density, g/cm3 10
8.5

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.1
Stiffness to Weight: Bending, points 13
19
Strength to Weight: Axial, points 3.4
7.4
Strength to Weight: Bending, points 5.4
9.7
Thermal Shock Resistance, points 6.6
7.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.050
Bismuth (Bi), % 0
0 to 0.090
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
78 to 85
Iron (Fe), % 0
0 to 0.3
Lead (Pb), % 0 to 0.0020
0.050 to 0.25
Nickel (Ni), % 0
0 to 0.5
Phosphorus (P), % 0 to 0.0020
0 to 0.050
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 99.95 to 100
0
Tin (Sn), % 0
1.5 to 4.5
Zinc (Zn), % 0 to 0.0010
12 to 20
Residuals, % 0
0 to 0.5