AWS BVAg-0 vs. C84200 Brass

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C84200 brass belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C84200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.33
Shear Modulus, GPa 26
40
Tensile Strength: Ultimate (UTS), MPa 130
250

Thermal Properties

Latent Heat of Fusion, J/g 110
180
Melting Completion (Liquidus), °C 960
990
Melting Onset (Solidus), °C 960
840
Specific Heat Capacity, J/kg-K 240
370
Thermal Expansion, µm/m-K 20
19

Otherwise Unclassified Properties

Density, g/cm3 10
8.5

Common Calculations

Stiffness to Weight: Axial, points 3.8
6.9
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 3.4
8.2
Strength to Weight: Bending, points 5.4
10
Thermal Shock Resistance, points 6.6
9.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
78 to 82
Iron (Fe), % 0
0 to 0.4
Lead (Pb), % 0 to 0.0020
2.0 to 3.0
Nickel (Ni), % 0
0 to 0.8
Phosphorus (P), % 0 to 0.0020
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 99.95 to 100
0
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
4.0 to 6.0
Zinc (Zn), % 0 to 0.0010
10 to 16
Residuals, % 0
0 to 0.7