AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C91700 bronze belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C91700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 26
41
Tensile Strength: Ultimate (UTS), MPa 130
330

Thermal Properties

Latent Heat of Fusion, J/g 110
190
Melting Completion (Liquidus), °C 960
1020
Melting Onset (Solidus), °C 960
850
Specific Heat Capacity, J/kg-K 240
370
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 10
8.7

Common Calculations

Stiffness to Weight: Axial, points 3.8
6.9
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 3.4
11
Strength to Weight: Bending, points 5.4
12
Thermal Shock Resistance, points 6.6
12

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
84.2 to 87.5
Iron (Fe), % 0
0 to 0.2
Lead (Pb), % 0 to 0.0020
0 to 0.25
Nickel (Ni), % 0
1.2 to 2.0
Phosphorus (P), % 0 to 0.0020
0 to 0.3
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 99.95 to 100
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
11.3 to 12.5
Zinc (Zn), % 0 to 0.0010
0 to 0.25