AWS BVAg-0 vs. R60804 Alloy

Both AWS BVAg-0 and R60804 alloy are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is R60804 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
98
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 26
36
Tensile Strength: Ultimate (UTS), MPa 130
430

Thermal Properties

Latent Heat of Fusion, J/g 110
250
Specific Heat Capacity, J/kg-K 240
270
Thermal Expansion, µm/m-K 20
6.0

Otherwise Unclassified Properties

Density, g/cm3 10
6.5

Common Calculations

Stiffness to Weight: Axial, points 3.8
8.3
Stiffness to Weight: Bending, points 13
23
Strength to Weight: Axial, points 3.4
18
Strength to Weight: Bending, points 5.4
19
Thermal Shock Resistance, points 6.6
53

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Chromium (Cr), % 0
0.070 to 0.13
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0
0.18 to 0.24
Lead (Pb), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 99.95 to 100
0
Tin (Sn), % 0
1.2 to 1.7
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
97.8 to 98.6
Residuals, % 0
0 to 0.12