AWS BVAg-29 vs. AWS BVPd-1
Both AWS BVAg-29 and AWS BVPd-1 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition.
For each property being compared, the top bar is AWS BVAg-29 and the bottom bar is AWS BVPd-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 150 |
| Poisson's Ratio | 0.37 | |
| 0.37 |
| Shear Modulus, GPa | 27 | |
| 56 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 240 |
Thermal Properties
| Brazing Temperature, °C | 710 to 790 | |
| 1240 to 1250 |
| Latent Heat of Fusion, J/g | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 710 | |
| 1240 |
| Melting Onset (Solidus), °C | 620 | |
| 1230 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 310 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.2 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 14 | |
| 16 |
| Strength to Weight: Axial, points | 5.2 | |
| 6.1 |
| Strength to Weight: Bending, points | 7.3 | |
| 7.9 |
| Thermal Shock Resistance, points | 8.8 | |
| 9.8 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Cobalt (Co), % | 0 | |
| 33.9 to 36 |
| Copper (Cu), % | 22.5 to 25.5 | |
| 0 |
| Indium (In), % | 14 to 15 | |
| 0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 to 0.0020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.060 |
| Palladium (Pd), % | 0 | |
| 64 to 66 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.0020 |
| Silver (Ag), % | 60.5 to 62.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 to 0.0010 |