AWS BVAg-31 vs. N07773 Nickel

AWS BVAg-31 belongs to the otherwise unclassified metals classification, while N07773 nickel belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-31 and the bottom bar is N07773 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 90
200
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 33
77
Tensile Strength: Ultimate (UTS), MPa 180
710

Thermal Properties

Latent Heat of Fusion, J/g 150
320
Melting Completion (Liquidus), °C 850
1510
Melting Onset (Solidus), °C 820
1460
Specific Heat Capacity, J/kg-K 280
450
Thermal Expansion, µm/m-K 18
13

Otherwise Unclassified Properties

Density, g/cm3 10
8.5

Common Calculations

Stiffness to Weight: Axial, points 4.9
13
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.9
23
Strength to Weight: Bending, points 7.0
21
Thermal Shock Resistance, points 7.8
20

Alloy Composition

Aluminum (Al), % 0
0 to 2.0
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0 to 0.030
Chromium (Cr), % 0
18 to 27
Copper (Cu), % 31 to 33
0
Iron (Fe), % 0
0 to 32
Lead (Pb), % 0 to 0.0020
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 5.5
Nickel (Ni), % 0
45 to 60
Niobium (Nb), % 0
2.5 to 6.0
Palladium (Pd), % 8.0 to 12
0
Phosphorus (P), % 0 to 0.0020
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 57 to 59
0
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 2.0
Tungsten (W), % 0
0 to 6.0
Zinc (Zn), % 0 to 0.0010
0