AWS BVAg-32 vs. ASTM B522 Class II

Both AWS BVAg-32 and ASTM B522 class II are otherwise unclassified metals. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is ASTM B522 class II.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
96
Poisson's Ratio 0.37
0.41
Shear Modulus, GPa 34
34
Tensile Strength: Ultimate (UTS), MPa 180
280 to 490

Thermal Properties

Latent Heat of Fusion, J/g 140
77
Melting Completion (Liquidus), °C 950
1030
Melting Onset (Solidus), °C 900
1030
Specific Heat Capacity, J/kg-K 270
160
Thermal Expansion, µm/m-K 17
15

Otherwise Unclassified Properties

Density, g/cm3 11
17

Common Calculations

Stiffness to Weight: Axial, points 4.9
3.1
Stiffness to Weight: Bending, points 14
8.9
Strength to Weight: Axial, points 4.7
4.4 to 7.8
Strength to Weight: Bending, points 6.7
5.5 to 8.0
Thermal Shock Resistance, points 8.0
13 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
0
Gold (Au), % 0
68.5 to 69.5
Lead (Pb), % 0 to 0.0020
0
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Platinum (Pt), % 0
5.5 to 6.5
Silver (Ag), % 53 to 55
24.5 to 25.5
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.26