AWS BVAg-32 vs. AWS BAg-33

Both AWS BVAg-32 and AWS BAg-33 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 46% of their average alloy composition in common. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is AWS BAg-33.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
85
Poisson's Ratio 0.37
0.32
Shear Modulus, GPa 34
32
Tensile Strength: Ultimate (UTS), MPa 180
170

Thermal Properties

Brazing Temperature, °C 950 to 980
680 to 840
Latent Heat of Fusion, J/g 140
130
Melting Completion (Liquidus), °C 950
680
Melting Onset (Solidus), °C 900
610
Specific Heat Capacity, J/kg-K 270
320
Thermal Expansion, µm/m-K 17
23

Otherwise Unclassified Properties

Density, g/cm3 11
8.6

Common Calculations

Stiffness to Weight: Axial, points 4.9
5.5
Stiffness to Weight: Bending, points 14
17
Strength to Weight: Axial, points 4.7
5.5
Strength to Weight: Bending, points 6.7
7.9
Thermal Shock Resistance, points 8.0
6.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
16.5 to 18.5
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
29 to 31
Lead (Pb), % 0 to 0.0020
0
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 53 to 55
24 to 26
Zinc (Zn), % 0 to 0.0010
26.5 to 28.5
Residuals, % 0
0 to 0.15