Both AWS BVAg-32 and class 2 tungsten are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is class 2 tungsten.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
260
Poisson's Ratio 0.37
0.28
Shear Modulus, GPa 34
100
Tensile Strength: Ultimate (UTS), MPa 180
860

Thermal Properties

Latent Heat of Fusion, J/g 140
160
Specific Heat Capacity, J/kg-K 270
120
Thermal Expansion, µm/m-K 17
4.6

Otherwise Unclassified Properties

Density, g/cm3 11
15

Common Calculations

Stiffness to Weight: Axial, points 4.9
9.6
Stiffness to Weight: Bending, points 14
14
Strength to Weight: Axial, points 4.7
16
Strength to Weight: Bending, points 6.7
13
Thermal Shock Resistance, points 8.0
52

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
0
Lead (Pb), % 0 to 0.0020
0
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 53 to 55
0
Tungsten (W), % 0
92.5
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
7.5