AWS BVAg-32 vs. CC493K Bronze

AWS BVAg-32 belongs to the otherwise unclassified metals classification, while CC493K bronze belongs to the copper alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is CC493K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
100
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 34
39
Tensile Strength: Ultimate (UTS), MPa 180
270

Thermal Properties

Latent Heat of Fusion, J/g 140
180
Melting Completion (Liquidus), °C 950
960
Melting Onset (Solidus), °C 900
880
Specific Heat Capacity, J/kg-K 270
360
Thermal Expansion, µm/m-K 17
19

Otherwise Unclassified Properties

Density, g/cm3 11
8.9

Common Calculations

Stiffness to Weight: Axial, points 4.9
6.5
Stiffness to Weight: Bending, points 14
18
Strength to Weight: Axial, points 4.7
8.6
Strength to Weight: Bending, points 6.7
11
Thermal Shock Resistance, points 8.0
10

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.3
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
79 to 86
Iron (Fe), % 0
0 to 0.2
Lead (Pb), % 0 to 0.0020
5.0 to 8.0
Nickel (Ni), % 0
0 to 2.0
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0 to 0.1
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 53 to 55
0
Sulfur (S), % 0
0 to 0.1
Tin (Sn), % 0
5.2 to 8.0
Zinc (Zn), % 0 to 0.0010
2.0 to 5.0