AWS BVAg-32 vs. CR003A Copper

AWS BVAg-32 belongs to the otherwise unclassified metals classification, while CR003A copper belongs to the copper alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is CR003A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
120
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 34
43
Tensile Strength: Ultimate (UTS), MPa 180
230

Thermal Properties

Latent Heat of Fusion, J/g 140
210
Melting Completion (Liquidus), °C 950
1090
Melting Onset (Solidus), °C 900
1040
Specific Heat Capacity, J/kg-K 270
390
Thermal Expansion, µm/m-K 17
17

Otherwise Unclassified Properties

Density, g/cm3 11
9.0

Common Calculations

Stiffness to Weight: Axial, points 4.9
7.2
Stiffness to Weight: Bending, points 14
18
Strength to Weight: Axial, points 4.7
7.1
Strength to Weight: Bending, points 6.7
9.3
Thermal Shock Resistance, points 8.0
8.1

Alloy Composition

Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
99.954 to 100
Iron (Fe), % 0
0 to 0.0010
Lead (Pb), % 0 to 0.0020
0 to 0.00050
Oxygen (O), % 0
0 to 0.040
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Selenium (Se), % 0
0 to 0.00020
Silver (Ag), % 53 to 55
0 to 0.0025
Sulfur (S), % 0
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Zinc (Zn), % 0 to 0.0010
0