MakeItFrom.com
Menu (ESC)

AWS BVAg-32 vs. C14700 Copper

AWS BVAg-32 belongs to the otherwise unclassified metals classification, while C14700 copper belongs to the copper alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is C14700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
120
Poisson's Ratio 0.37
0.34
Shear Modulus, GPa 34
43
Tensile Strength: Ultimate (UTS), MPa 180
240 to 320

Thermal Properties

Latent Heat of Fusion, J/g 140
210
Melting Completion (Liquidus), °C 950
1080
Melting Onset (Solidus), °C 900
1070
Specific Heat Capacity, J/kg-K 270
390
Thermal Expansion, µm/m-K 17
17

Otherwise Unclassified Properties

Density, g/cm3 11
8.9

Common Calculations

Stiffness to Weight: Axial, points 4.9
7.2
Stiffness to Weight: Bending, points 14
18
Strength to Weight: Axial, points 4.7
7.3 to 10
Strength to Weight: Bending, points 6.7
9.5 to 12
Thermal Shock Resistance, points 8.0
8.4 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
99.395 to 99.798
Lead (Pb), % 0 to 0.0020
0
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0.0020 to 0.0050
Silver (Ag), % 53 to 55
0
Sulfur (S), % 0
0.2 to 0.5
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.1