AWS BVAg-32 vs. C87600 Bronze

AWS BVAg-32 belongs to the otherwise unclassified metals classification, while C87600 bronze belongs to the copper alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is C87600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
110
Poisson's Ratio 0.37
0.33
Shear Modulus, GPa 34
42
Tensile Strength: Ultimate (UTS), MPa 180
470

Thermal Properties

Latent Heat of Fusion, J/g 140
280
Melting Completion (Liquidus), °C 950
970
Melting Onset (Solidus), °C 900
860
Specific Heat Capacity, J/kg-K 270
410
Thermal Expansion, µm/m-K 17
17

Otherwise Unclassified Properties

Density, g/cm3 11
8.5

Common Calculations

Stiffness to Weight: Axial, points 4.9
7.4
Stiffness to Weight: Bending, points 14
19
Strength to Weight: Axial, points 4.7
16
Strength to Weight: Bending, points 6.7
16
Thermal Shock Resistance, points 8.0
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
88 to 92.5
Lead (Pb), % 0 to 0.0020
0 to 0.5
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Silicon (Si), % 0
3.5 to 5.5
Silver (Ag), % 53 to 55
0
Zinc (Zn), % 0 to 0.0010
4.0 to 7.0
Residuals, % 0
0 to 0.5